UHP 350mm Elektroda Grafit Ing Elektrolisis Kanggo Smelting Steel
Parameter teknis
| Parameter | Part | Unit | UHP 350mm (14") Data |
| Diameter nominal | Elektroda | mm (inci) | 350(14) |
| Diameter Max | mm | 358 | |
| Diameter Min | mm | 352 | |
| Panjang Nominal | mm | 1600/1800 | |
| Max Length | mm | 1700/1900 | |
| Min Length | mm | 1500/1700 | |
| Kapadhetan Saiki Max | KA/cm2 | 20-30 | |
| Kapasitas Ngangkut Saiki | A | 20000-30000 | |
| Resistance spesifik | Elektroda | μΩm | 4.8-5.8 |
| Puting susu | 3.4-4.0 | ||
| Kekuatan lentur | Elektroda | Mpa | ≥12.0 |
| Puting susu | ≥22.0 | ||
| Modulus Young | Elektroda | Gpa | ≤13.0 |
| Puting susu | ≤18.0 | ||
| Kapadhetan Bulk | Elektroda | g/cm3 | 1.68-1.72 |
| Puting susu | 1.78-1.84 | ||
| CTE | Elektroda | × 10-6/ ℃ | ≤1.2 |
| Puting susu | ≤1.0 | ||
| Kandungan Ash | Elektroda | % | ≤0.2 |
| Puting susu | ≤0.2 |
CATETAN: Sembarang syarat tartamtu ing ukuran bisa ditawakake.
Grade produk
Gelar elektroda grafit dipérang dadi elektroda grafit daya biasa (RP), elektroda grafit daya dhuwur (HP), elektroda grafit daya dhuwur (UHP).
Aplikasi Utamane Kanggo Tungku Busur Listrik Ing Pembuatan Baja
Elektroda grafit kanggo nggawe baja 70-80% saka total aplikasi elektroda grafit. Kanthi maringaken voltase dhuwur lan saiki kanggo elektroda grafit, busur listrik bakal kui antarane tip elektroda lan kethokan logam kang bakal gawé panas ageng kanggo nyawiji kethokan. Proses peleburan bakal ngonsumsi elektroda grafit, lan kudu diganti terus-terusan.
Elektroda grafit UHP umume digunakake ing industri baja sajrone produksi baja tungku busur listrik (EAF). Proses EAF nyakup leleh baja kethokan kanggo ngasilake baja anyar. Elektroda grafit UHP digunakake kanggo nggawe busur listrik, sing dadi panas baja kethokan nganti titik leleh. Proses iki efisien lan biaya-efektif, amarga ngidini baja bisa diprodhuksi kanthi cepet lan kanthi jumlah akeh.
Tampilan bagean lan tampilan rencana saka Tungku Busur Listrik
We are Pabrik diduweni baris produksi lengkap lan tim profesional.
30% TT ing advance minangka pembayaran mudhun, The 70% imbangan TT sadurunge pangiriman.
produk sing gegandhengan
-
Elektroda Grafit Gunakake Kanggo Pemurnian Korundum...
Bagan Parameter Teknis 1: Parameter Teknis Kanggo Diameter Elektroda Grafit Diameter Kecil Ketahanan Bagian Kekuwatan Fleksibel Kapadhetan Modulus Muda CTE Ash Inch mm μΩ·m MPa GPa g/cm3 ×10-6/℃ % 3 75 Elektroda 7.5-8.5 ≥9.3 ≤9.0 ≤ -1.64 ≤2.4 ≤0.3 Puting 5.8-6.5 ≥16.0 ≤13.0 ≥1.74 ≤2.0 ≤0.3 4 100 Elektroda 7.5-8.5 ≥9.0 ≤9.3 1.55-1.64...
-
Tempel Elektroda Karbon Soderberg kanggo Ferroallo...
Item Parameter Teknis Disegel Elektroda Past Standar Tempel Elektroda GF01 GF02 GF03 GF04 GF05 Fluks Volatile(%) 12.0-15.5 12.0-15.5 9.5-13.5 11.5-15.5 11.5-15.5 11.5-15.5 11.5-15.5 Kompres 22.0 21.0 20.0 Resisivity(uΩm) 65 75 80 85 90 Kapadhetan Volume(g/cm3) 1.38 1.38 1.38 1.38 1.38 Elongation(%) 5-20 5-20 5-40 15-40 15-40 % ...
-
Dhuwur Kapadhetan cilik Diameter Tungku Grafit El ...
Bagan Parameter Teknis 1: Parameter Teknis Kanggo Diameter Elektroda Grafit Diameter Kecil Ketahanan Bagian Kekuwatan Fleksibel Kapadhetan Modulus Muda CTE Ash Inch mm μΩ·m MPa GPa g/cm3 ×10-6/℃ % 3 75 Elektroda 7.5-8.5 ≥9.3 ≤9.0 ≤ -1.64 ≤2.4 ≤0.3 Puting 5.8-6.5 ≥16.0 ≤13.0 ≥1.74 ≤2.0 ≤0.3 4 100 Elektroda 7.5-8.5 ≥9.0 ≤9.3 1.55-1.64...
-
Daya Biasa Elektroda Grafit Diameter Cilik...
Bagan Parameter Teknis 1: Parameter Teknis Kanggo Diameter Elektroda Grafit Diameter Kecil Ketahanan Bagian Kekuwatan Fleksibel Kapadhetan Modulus Muda CTE Ash Inch mm μΩ·m MPa GPa g/cm3 ×10-6/℃ % 3 75 Elektroda 7.5-8.5 ≥9.3 ≤9.0 ≤ -1.64 ≤2.4 ≤0.3 Puting 5.8-6.5 ≥16.0 ≤13.0 ≥1.74 ≤2.0 ≤0.3 4 100 Elektroda 7.5-8.5 ≥9.0 ≤9.3 1.55-1.64...
-
Elektroda Grafit Tungku Diameter Cilik 75mm...
Bagan Parameter Teknis 1: Parameter Teknis Kanggo Diameter Elektroda Grafit Diameter Kecil Ketahanan Bagian Kekuwatan Fleksibel Kapadhetan Modulus Muda CTE Ash Inch mm μΩ·m MPa GPa g/cm3 ×10-6/℃ % 3 75 Elektroda 7.5-8.5 ≥9.3 ≤9.0 ≤ -1.64 ≤2.4 ≤0.3 Puting 5.8-6.5 ≥16.0 ≤13.0 ≥1.74 ≤2.0 ≤0.3 4 100 Elektroda 7.5-8.5 ≥9.0 ≤9.3 1.55-1.64...
-
Low Sulfur FC 93% Carburizer Carbon Raiser Iro...
Grafit Petroleum Coke (GPC) Komposisi Karbon Tetap(FC) Volatile Matter(VM) Sulfur(S) Ash Nitrogen(N) Hidrogen(H) Kelembapan ≥98% ≤1% 0≤0.05% ≤1% ≤0.03% ≤0.01% ≤0,5% ≥98,5% ≤0,8% ≤0,05% ≤0,7% ≤0,03% ≤0,01% ≤0,5% ≥99% ≤0,5% ≤0,03% ≤0,5% ≤0,03% ≤0,03% ≤ 0,03% ≤% ≤0,5% 0-0.50mm, 5-1mm, 1-3mm, 0-5mm, 1-5mm, 0-10mm, 5-10mm, 5-10mm, 10-15mm utawa ing pilihan pelanggan Packing: 1. Waterproof ...